Title:
The Preparation and Characterization for High-Strength Electrospun Polyimide/Ag Composite Nanofibres
作者:
简绍菊;胡晓婺;邹燕;陈水亮;侯豪情
1. 武夷学院环境与建筑工程系, 福建 武夷山 354300; 2. 江西师范大学化学化工学院, 江西 南昌 330022
Author(s):
JIAN Shao-ju;  HU Xiao-wu;  ZOU Yan;  CHEN Shui-liang;  HOU Hao-qing
关键词:
聚酰亚胺;  银;  静电纺丝;  力学性能
Keywords:
polyimide;  silver;  electrospinning;  mechanical properties
分类号:
TB 331
文献标志码:
A
摘要:
采用电纺及热亚胺化技术制备了聚酰亚胺/Ag纳米纤维复合材料, 用X-射线衍射(XRD)、扫描电子显微镜(SEM)及透射电子显微镜(TEM)对纤维表面形貌及结构进行了表征, 并研究其电学性能及力学性能. 结果显示, 随着Ag含量的增加, 复合纳米纤维膜的电导率逐渐提高. 当Ag的质量分数为35%时, 复合纳米纤维膜的导电率为2.8 μs/cm, 同时其拉伸强度高达240 MPa.
Abstract:
Silvered/polyimide composite nanofibres were fabricated from the poly(amic acid) (BPDA-BPA-ODA) by electrospinning and thermal imidization. The morphology and structure of electrospun fiber mat were characterized by X-ray diffraction, scanning and transmission electron microscopes. Experimental results show that the electronic conductivity of the composites increased with increase of silver content and reached up to 2.8 μs/cm and 240 MPa, respectively with silver content of 35%.

参考文献/References:

[1] Kim B S, Bae S H, Park Y H. Preparation and characterization of polyimide/carbon-nanotube composites [J]. Macromol Res, 2007, 15(4): 357-362.
[2] Auman B C, Chen Yujean, Huang Shengyu, et al. Highly adheresive polyimide copper clad laminate and method of making the same [P]. U S P, 2009: 428458.
[3] Senturia S D. Polyimides in microelectronics [M]. American Chemical Society, 1987: 428-436.
[4] Berger. Polyimide containing silicones as protective coating on semiconductor device [P]. U S P, 1977: 4030948.
[5] Southward R E, Thompson D W. Synthesis of silvered polyimide films prepared from silver(I) complexes and BPDA/4,4?-ODA [J]. Chem Mater, 2004, 16: 1277-1284.
[6] Southward R E, Thompson D S, Thompson D W. Inverse chemical vapor deposition: A novel single stage synthesis of highly reflective and conductive silvered polymeric films [J]. Chem Mater, 1999, 11: 501-507.
[7] 吴战鹏, 武德珍, 齐胜利, 等. 聚酰亚胺结构对聚酰亚胺银复合薄膜的反射和导电性能的影响 [J]. 高分子材料科学与工程, 2006, 22(1): 95-98.
[8] Huang Gaobo, Chen Shuiliang, Lai Chuilin, et al. Electrospun polymer nanofibres with small diameters [J]. Nanotechnology, 2006, 17: 1558-1563.
[9] Chuangchote S, Supaphol P. Fabrication of aligned poly(vinyl alcohol) nanofibers by electrospinning [J]. J Nanosci Nanotechnol, 2006, 6:125-129.
[10] Duan Gaigai, Jiang Shaohua, Chen Shuiliang, et al. Heat and solvent resistant electrospun polybenzoxazole nanofibers from methoxy-containing polyaramide [J]. Journal of Nanomaterials, 2010: 219562-219567.
[11] Huang Chaobo, Chen Shuiliang, Darrell H, et al. High-strength mats from electrospun poly(p-phenylene biphenylteracarboximide) nanofibers [J]. Advanced Materials, 2006, 18: 668-671.
[12] Chen Shuiliang, Hu Ping, Cheng Chuyun, et al. Electrospun nanofiber belts made from high performance copolyimide [J]. Nanotechnology, 2008, 19: 1-9.
[13] Deitzel J M, Kleinmeyer J, Hirvonen J K, et al. Controlled deposition of electrospun poly(ethylene oxide) fibers [J]. Polymer, 2001, 42: 8163-8170.

更新日期/Last Update: 1900-01-01