[1]方卢秋,李秋.脱水污泥活性炭的制备及其吸附特性研究[J].江西师范大学学报(自然科学版),2013,(03):306-309.
 FANG Lu-qiu,LI Qiu.Study on Absorption Characteristic and Preparation of Dewatered Sludge Active Carbon[J].,2013,(03):306-309.
点击复制

脱水污泥活性炭的制备及其吸附特性研究()
分享到:

《江西师范大学学报》(自然科学版)[ISSN:1006-6977/CN:61-1281/TN]

卷:
期数:
2013年03期
页码:
306-309
栏目:
出版日期:
2013-05-01

文章信息/Info

Title:
Study on Absorption Characteristic and Preparation of Dewatered Sludge Active Carbon
作者:
方卢秋;李秋
长江师范学院化学化工学院,重庆,408100;重庆西彭镇第一中学,重庆,401326
Author(s):
FANG Lu-qiu;LI Qiu
关键词:
脱水污泥脱水污泥活性炭制备吸附特性碘吸附值
Keywords:
dewatered sludgedewatered sludge active carbonpreparationabsorption characteristiciodine absorption value
分类号:
TQ424.1;X788
文献标志码:
A
摘要:
以城市污水处理厂产生的脱水污泥为原料,采用化学活化法并结合传统的直接加热技术制备脱水污泥活性炭,研究了影响脱水污泥活性炭吸附特性的各种因素.研究结果表明:制备脱水污泥活性炭的优化条件是活化剂为5 mol·L-1ZnCl2+5 mol·L-1 H2SO4混合溶液,固液比为1∶2.5,复配比为2∶1,浸渍时间为24h,活化温度为600℃,活化时间为20 min.制备的脱水污泥活性炭碘吸附值为939.7 mg ·g-1,产率为69.03;,其吸附特性优于商品活性炭.
Abstract:
Dewatered sludge active carbon was prepared by dewatered sludge of municipal wastewater treatment plant adopting chemical activation method combined with direct pyrogenation technology.Various factors influenced the absorption characteristic of dewatered sludge active carbon was investigated carefully.The results show that:optimization condition of preparation dewatered sludge active carbon is 5 mol·L ZnCl2+5 mol·L H2SO4 compound solution as activation reagen,solid-liquid ratio is 1:2.5,ratio of ZnCl2: H2SO4 is 2:1,soakaging time is 24 h,activation temperature is 600 ℃,activation time is 20 min.Iodine absorption value of dewatered sludge active carbon using method proposed to preparate is 939.7 mg·g,produce ratio is 69.03%,absorption characteristic excelled merchandise active carbon.

参考文献/References:

[1] 梁鹏,黄霞,钱易.污泥减量化技术的研究进展 [J].环境污染治理技术与设备,2003,4(1):44-52.
[2] 张树国,吴志超,张善发,等.上海市污水处理厂污泥处置对策研究 [J].环境工程,2004,22(1):75-78.
[3] 蔺丽丽,蒋文举,金燕,等.微波法制备污泥活性炭研究 [J].环境工程学报,2007,1(4):119-122.
[4] 任爱玲,王启山,郭斌.污泥活性炭的结构特征及表面分形分析 [J].化学学报,2006,64(10):1068-1072.
[5] Zhang Fushen,Jerome O Nriagu,Hideaki Itoh.Mercury removal from water using activated carbons derived from organic sewage sludge [J].Water Res,2005,39:389-395.
[6] Hu Zhonghua.Novel activation process for preparing highly microporous and mesoporous activated carbons [J].Carbon,2001,39(6):877-886.
[7] Rio S,Faur Brasquet Cathenne,LeCoq L,et a1.Preparation and characterization of activated carbon from sewage sludge:Carbonization step [J].Water Science and Technology,2004,49(1):139-146.
[8] Chen Xiage,Jeyaseelan S,Graham N.Physical and chemical properties study of the activated carbon made from savage sludge [J].Waste Management,2002,22(7):755-760.
[9] 吕春祥,李开喜.沥青基球状活性炭的医用性能评价 [J].新型活性炭,2002,17(3):11-14.

备注/Memo

备注/Memo:
重庆市教育委员会科学技术研究(KJ071304)
更新日期/Last Update: 1900-01-01