Title:
A Soluble Poly(Aryl Ether Ether Ketone) Based on a New Bisphenol Containing Fluorine and Pyridine Groups
作者:
邓惠芳;刘晓玲;程立技;姜建文;盛寿日
江西师范大学化学化工学院,江西南昌,330022
Author(s):
DENG Hui-fang；LIU Xiao-ling；CHENG Li-ji；JIANG Jian-wen；SHENG Shou-ri
关键词:
4-(4-三氟甲基苯基)-2; 6-二(4-羟基苯基)吡啶; 氟化含吡啶结构聚醚醚酮; 合成; 表征
Keywords:
4-(4-trifluoromethylphenyl)-2; 6-bis (4-hydrophenyl) pyridine; fluorinated poly (aryl ether ether ketone) containing pyridine structure; synthesis; characterization
分类号:
O633.22
文献标志码:
A
摘要:
以4-三氟甲基苯甲醛、4'-羟基苯乙酮为主要原料,通过改进的Chichibabin反应合成了一种新型的双酚单体——4-(4-三氟甲基苯基)-2,6-二(4-羟基苯基)吡啶,继而将其与4,4'-二氟二苯酮进行缩聚反应,合成了一种主链含氟和2,6-二苯基吡啶结构的聚醚醚酮,并以FTIR、DSC、WAXD等对其结构和性能进行了表征.研究结果表明:聚合物的对数比浓黏度为0.65 dL·g-1,耐热性优异,所得聚醚醚酮玻璃化转变温度(Tg)为178℃,在空气中,5；的热失重温度为556℃,拉伸强度为99.5 MPa,杨氏膜量为3.01 GPa,断裂伸长率为14；.同时,该聚合物为无定形结构,在常温下可溶于N-甲基吡咯烷酮、N,N-二甲基乙酰胺、四氢呋喃和氯仿等有机溶剂中,介电常数为2.62(1 MHz),吸水率为0.46；.
Abstract:
A new bisphenol monomer,4-(4-trifluoromethylphenyl)-2,6-bis(4-hydrophenyl)pyridine was synthesized by a modified Chichibabin reaction using 4-trifluoromethylbenzaldehyde and 4'-hydroacetophenone as main original materials,which was then employed to prepare a new poly(aryl ether ether ketone)(PEKK)containing fluorine and 2,6-diphenylpyridine groups via aromatic nucleophilic substitution polycondensation with 4,4'-difluorobenzophenone,and their structure and properties were studied using analysis techniques such as FTIR,DSC and WAXD.The results indicated the resulting PEKK with inherent viscosities of 0.65 dL·g had excellent heat resistance with glass transition temperature of 178 ℃,5% weight loss decomposition temperature of 556 ℃ in air.In the meantime,the new fluorinated PEKK showed a 99.5 MPa tensile strengh,3.01 GPa Young's modulus and 14% elongations at break.Besides,this new PEEK with lower dielectric constant of 2.62(100 MHz)and low water absorption 0.46% was amorphous and was soluble in dipolar aprotic solvents such as N-methyl-2-pyrrolidone and N,N-dimethylacetamide,and some common organic solvents like chloroform and THF at room temperature.

参考文献/References:

[1] Attwood T E,Dawson P C,Freeman J L,et al.Synthesis and properties of polyaryletherketones [J].Polymer,1981,22(8):1096-1103.
[2] Rao V L.Polyether ketones [J].J Macromol Sci Rev Macromol Chem Phys,1995,C35(4):661-712.
[3] Wen Hongli,Song Caisheng,Tong Yongfen,et al.Synthesis and properties of poly(aryl ether sulfone ether ketone ketone)(PESEKK)[J].J Appl Polym Sci,2005,96(2):489-493.
[4] 刘晓玲,林淑英,罗秋燕,等.新型甲基取代的聚芳醚酮醚砜醚酮无规共聚物的合成与表征 [J].江西师范大学学报:自然科学版,2005,29(3):189-192.
[5] 余雯雯,宋铮,祝志芳,等.含间位苯基及芳酯基侧基聚芳醚酮的合成与表征 [J].江西师范大学学报:自然科学版,2010,34(5):520-524.
[6] Zhao Xiulan,Zhang Qin,Xue Lixin,et al.Preparation and gel properties of poly(ether ether ketone)with pendent sulfonimide groups [J].J Appl Polym Sci,2013,130(2):1058-1063.
[7] Chen Xiaoting,Sun Hao,Tang Xudong,et al.Synthesis and properties of novel phosphorus-containing poly(ether ether ketone ketone)s [J].J Appl Polym Sci,2008,110(3):1304-1309.
[8] Cheng Lin,Ying Lei,Feng Juan,et al.Novel heterocyclic poly(arylene ether ketone)s:Synthesis and polymerization of 4-(4'-hydroxyaryl)(2H)phthalazin-1-ones with methyl groups [J].J Polym Sci,Part A:Polym Chem,2007,45(8):1525-1535.
[9] 张莹,刘佰军,张云鹤,等.高Tg含萘聚芳醚酮的合成与性能 [J].高等学校化学学报,2008,29(7):1498-1500
[10] Liu Baiyun,Hu Wei,Chen Chunhua,et al.Soluble aromatic poly(ether ketone)s with a pendant 3,5-ditrifluoromethylphenyl group [J].Polymer,2004,45(10):3241-3247.
[11] Niu Yaming,Zhu Xiaoliang,Liu Lingzhi,et al.Synthesis and characterization of poly(aryl ether ketone)with trifluoromethyl-substituted benzene in the side chain [J].React Funct Polym,2006,66(5):559-566.
[12] Yao Huling,Sheng Shouri,Jiang Jianwen,et al.Soluble copoly(aryl ether ether ketone ketone)s containing xthanene and hexafluoroisopropylidene moieties [J].J Fluorine Chem,2012(144):176-181.
[13] 王忠刚,陈天禄,徐纪平.含不同取代基的Cardo 聚芳醚酮的合成及表征 [J].高分子学报,1995,38(4):494-498.
[14] Kawasaki S,Yamada M,Kobori K,et al.Synthesis and chemical,physical,and optical properties of 9,9-diarylfluorene-based poly(ether-ether-ketone)[J].Macromolecules,2007,40(15):5284-5289.
[15] Honkhambe P N,Pasale S K,Bhairamadgi N S,et al.Poly(ether ether ketone)s and poly(ether ether ketone ketone)s containing cardo decahydronaphthalene groups:Synthesis and characterization [J].J Appl Polym Sci,2011,122(3):1 607-1 613.

备注/Memo

备注/Memo:
国家自然科学基金(21064003,51163008)；江西省主要学科学术和技术带头人培养计划(20113BCB22012)；江西省自然科学基金(20114BAB203014,20132BAB206031)
更新日期/Last Update: 1900-01-01